20Kg/group,packed in a iron drum.
performance features of crusher liner plate wear resistant protective filling adhesive:
Before curing: with good fluidity and strong filling ability,easy to operate,safety and environmental protection
After curing: with low shrinking percentage and good adhesion,bearing capacity is high,can tear down
Can cure at the low temperature of -5 degree
With high impact resistant ability,especially suitable for the lining plate filling of coarse broken gyration type crusher
BD66 crusher liner plate anti wear filling material product usage:
BD66 crusher filling material (backing adhesives) is used in the filling/supporting between crusher lining plate and substrates,gravel barrels and jacket clearance,support cone and protective layer space,at the same time it can be used as buffer material,when the equipment suffers impacting or load vibration from broken ore, also used in the structural reinforcement,impact resistant vibration of ball mill wear resistant lining plate and cylinder clearance.
BD66 crusher lining plate special backing adhesives performance index:
Polyurethane modified epoxy material,two component ,red fluid
Color: A component: light red, B component: light yellow
Viscosity: A component: 1000, B component: 700mPa.s(GB/T2791-1995)
Density:A component: 1.5, B component: 1.06g/cm3 (GB/T13354-1992)
Compressive strength after curing:130 Mpa (GB/T2791-1995)
Shear strength after curing:10.1 Mpa (GB/T7124-1996)
Hardness after curing:Shore A90 (GB/T2144-1980)
Shrinkage ratio after curing: 0.01%
Cooperation ratio(A : B),weight ratio 5:1,volume ratio 3.2:1
Pot life:15 min,the shortest curing time before operation:24h
Operation temperature:5 to 30 degree
The temperature resistant after curing:-60 to100 degree
Impact resistant test:Using 50 tons air hammer to hammer the 50 stone for 5 times,the stone is not dehiscent.