Packing specification of BD726 high temperature wear resistant coatings:
Two component,10Kg/group,packed in a plastic drum
performance feature of BD726 high temperature corrosion resistant coating:
dark gray paste,large particle,room temperature curing,the curing product is the high temperature resistant
Excellent in wear & corrosion resistance
BD726 high temperature corrosion resistant coating and the metal substrate with high bonding strength
Convenient for construction,without very high technical requirements for constructors
It's not precipitated and hierarchical
Suitable for the protecting of high temperature wear,corrosion working condition
Hot water resistant,steam resistant,acid resistant,alkali resistant
Can do blade coating directly for both facade and ceiling,don't drip and slip,without the support
product usage of BD726 anti corrosive abrasion resistant coatings:
BD726 high temperature wear & corrosion resistant coatings is the high performance high-temperature & wear & corrosion resistant polymeric ceramic material compounded by high performance wear resistant,corrosion resistant material (like ceramic,silicon carbide,carborundum,titanium alloy etc.) and modified toughening heat resistant resin.Widely used in the preparation of wear & corrosion resistant coating on the surface of various machine part which has high temperature,wear resistant,corrosion resistant requirements.The highest temperature resistant is 250 degree
How to use of BD726 anti wear high temperature resistant coating:
1.Surface treatment:Do coarsening treatment on the pending-repair part,grinding with angle grinder or sand blasting etc,the surface after coarsening treatment should be cleaned,the surface after this treatment should be the one coarsening,dry and fresh substrates,should be no greasy dirt and dust.
2.Preparation:According to weight ratio 4:1,make A and B two components mix uniformly,and use it up within 40 min.Generally it’s while construction and configuration.Every time the most configuration quantity is not more than 2Kg,too much adhesive is solidified too fast,hasn’t been used up until the adhesive has partial solidified and can’t be used.According to the actual temperature,configuration can be properly a little more in winter and proper less in summer.If the temperature is too low,can properly heat up the A component to reduce viscosity for easy to configure.
3.Coating:The suitable coating thickness of BD726 high temperature wear & corrosion resistant coatings is 4-8mm.Make the mixed-up material be coating on the pending-repair part layer by layer,the first layer should be compacted,make it infiltrate fully with the substrates.Repair the surface to be smooth after the coating is coated in the suitable size,or make low viscosity wear resistant adhesive be coating on the coating surface.This material can’t do machining,should pay attention to controlling the coating thickness to avoid appearing interference phenomenon in the assembly.
4.Curing: Cure for 24 hours at the temperature of 25 degree before using,if the temperature is low,should heat it up or prolong curing time to promote the curing.General construction in winter,can use iodine tungsten lamp do irradiation heating with 40cm distance from the coating.
|BD726 Physical mechanical properties table
|tensile strength (kg/cm2) GB6329-86
||bending strength(kg/cm2) GB1042-79
||hardness after curing(Shore D)
Transportation storage of BD726 anti corrosion high temperature resistant coatings:
|BD726 curing features table(test condition:temperature:20～25℃,relative humidity:55)
||operation time limit(25℃)
||working temperature of ensuring wear resistance(℃)
1.Sealed storage in the cool and dry place.The warranty period is 1 year.
2.Avoid placing it upside down,knocking against and transporting it as a non-dangerous product during transportation.